Crystal growth, optical and scintillation properties of Nd3+ doped GdTaO4 single crystal

Publication date: 15 November 2014
Source:Journal of Crystal Growth, Volume 406
Author(s): Fang Peng , Wenpeng Liu , Qingli Zhang , Huajun Yang , Chaoshu Shi , Rihua Mao , Dunlu Sun , Jianqiao Luo , Guihua Sun
A new Nd³⁺ doped GdTaO4 crystal (having density of 8.83gcm⁻³) was successfully grown by the Czochralski method. The as-grown crystal was with dimension of Φ30mm×50mm. The structure parameters were refined by Rietveld method to X-ray powder diffraction. The photoluminescence spectra including emission, excitation and decay curves were measured. The photoluminescence decay times were determined to be 20.7ns (7.73%) and 496ns (92.27%) monitored at 417nm, and 463ns monitored at 453nm, respectively. In addition, the radioluminescence spectrum was given and discussed. The scintillation decay constants were 46.4ns (48%) and 1199.7ns (52%). Compared with GdTaO4, the scintillation decay of Nd:GdTaO4 was faster and the percent of the fast component was remarkably increased. Besides, the light yield of Nd:GdTaO4 can be estimated to be equal to that of GdTaO4. All these results suggest that the Nd:GdTaO4 crystal can be expected as a potential heavy and fast scintillator.